LZM WaterFine Glass Baking Paint
I Product overview
◆Category: This product is one/two-component baking paint with high-grade resin as film material;
◆Constitution: High-grade resin, pigment, packing material, addictives, water, etc.;
◆Characteristics:
※Water is the disperse medium of this product, nonflammable and nonexplosive at normal temperature;
※Fine adhesion, weatherability, protection and decoration performance;
※No poisonous or toxic substances produced in the course of construction and film formation, environmental friendly and according with the instruction RoHs of European Union.
II Scope of application: apply for surface coating of household glass and ceramics.
III Technical data (typical data)
|
Item |
Indicator |
|
Color and appearance |
Thick liquid of different color |
|
Fineness |
≤20μm |
|
PH value |
8.0~9.0 |
|
Viscosity (paint-4cup) |
≥30s |
|
Solid content (120°C /2 hour) |
≥32% (true color) |
|
Gloss (60° photometer) |
0~90 |
|
Adhesion (Grid method) |
≤5% paint off |
|
Pencil hardness |
≥3H |
|
Resistivity against water (dip in tap water at normal temperature) |
No blistering, peeling, or discoloration in 7 days |
|
Resistance to essences (point contact) |
No blistering, peeling, or discoloration in 10h |
|
Alcohol resistance (95% absolute alcohol) |
No peeling with grid method after dipping for 12h |
|
Wine resistance (alcoholic strength: 52% vol wine) |
No peeling with grid method after dipping for 24h |
(Note: test conditions for resistance to water, alcohol, wine and essences: 1. Substrate: wipe cleaned glass plate with alcohol; 2. Coating: spray coating, dry film 15μm~20μm; 3. Drying: 180±2°C, baking at constant temperature for 30min.)
IV Construction for reference
◆Surface treatment: wipe off the impurity, for example, floating dust, oil stain, etc. to keep the surface clean and dry;
◆Form of construction work: spray coating;
◆Thinner: purified water or clean tap water;
◆Dilution ratio: add water by 5%~10% of the paint weight, or adjust as the case may be;
◆Applicable viscosity: immersion 25~30s (paint-4cup, 23±2°C);
◆Type of drying: bake at a constant temperature of 180±2°C for 30 min;
◆Coating thickness: 10μm ~20μm (dry film thickness, single layer).
VII Attentions
◆Difference in the level of processing substrate is referred to final effect and barrier property of the film coating;
◆After coating, let work pieces sit in dustless environment for 5~10min before accessing baking equipment;
◆Keep the product in a cool and ventilate place (0°C~45°C). The validity is half a year. If failing to meet the time limit, the product still can be used if proved to be up to standard through inspection.
VI Packing and shipping
◆Packing: 20kg/barrel or 50kg/barrel;
◆Shipping: transport as non-hazardous goods. |